Valox 420SEO
| 厂家(产地)： | 沙伯基础sabic | 密度： | 1.6 | 吸水率： | 0.06 |
| 牌号： | 420SEO | 类型： | 标准料 | 硬度： | 119 |
| 规格级别： | 注塑 | 用途： | 切边机、食物搅拌机、马达定子、开关等 | 缺口冲击强度： | 64 |
| 弯曲模量： | 7579 | 属性： | 属性值 | ||
| 查看全部参数> | |||||
@Temperature 23.0 °C0.0900 %
@Temperature 73.4 °FISO 62Linear Mold Shrinkage, Flow0.00100-0.00500cm/cm0.00100-0.00500in/inon tensile bar; SABIC Method0.00500-0.00700cm/cm
@Thickness 3.20 mm0.00500-0.00700in/in
@Thickness 0.126 inSABIC MethodLinear Mold Shrinkage, Transverse0.00400-0.00800cm/cm0.00400-0.00800in/inon tensile bar; SABIC Method0.00500-0.0100cm/cm
@Thickness 3.20 mm0.00500-0.0100in/in
@Thickness 0.126 inSABIC MethodMelt Flow29.0g/10 min
@Load 5.00 kg,
Temperature 250 °C29.0g/10 min
@Load 11.0 lb,
Temperature 482 °F[cm^3/10 min] Melt Volume Rate; ISO 113342.0g/10 min
@Load 5.00 kg,
Temperature 250 °C42.0g/10 min
@Load 11.0 lb,
Temperature 482 °FASTM D 1238Mechanical PropertiesMetricEnglishCommentsHardness, Rockwell R119119ASTM D 785119119ISO 2039-2Hardness, H358/30118MPa17100psiISO 2039-1Tensile Strength at Break120MPa17400psiType I, 5 mm/min; ASTM D 638120MPa17400psi5 mm/min; ISO 527Tensile Strength, Yield120MPa17400psiType I, 5 mm/min; ASTM D 638120MPa17400psi5 mm/min; ISO 527Elongation at Break1.90 %1.90 %5 mm/min; ISO 5272.00 %2.00 %Type I, 5 mm/min; ASTM D 638Elongation at Yield1.90 %1.90 %5 mm/min; ISO 5272.00 %2.00 %Type I, 5 mm/min; ASTM D 638Tensile Modulus10.0GPa1450ksi1 mm/min; ISO 52712.0GPa1740ksi5 mm/min; ASTM D 638Flexural Modulus9.50GPa1380ksi2 mm/min; ISO 1789.80GPa1420ksi1.3 mm/min, 50 mm span; ASTM D 790Flexural Strength180MPa26100psiISO 178186MPa27000psibrk, 1.3 mm/min, 50 mm span; ASTM D 790Izod Impact, Unnotched6.20J/cm
@Temperature 23.0 °C11.6ft-lb/in
@Temperature 73.4 °FASTM D 4812Izod Impact, Unnotched (ISO)45.0kJ/m²
@Temperature 23.0 °C21.4ft-lb/in²
@Temperature 73.4 °F80*10*4; ISO 180/1U45.0kJ/m²
@Temperature -30.0 °C21.4ft-lb/in²
@Temperature -22.0 °F80*10*4; ISO 180/1UCharpy Impact Unnotched5.00J/cm²
@Temperature 23.0 °C23.8ft-lb/in²
@Temperature 73.4 °FEdgew 80*10*4 sp=62mm; ISO 179/1eU5.00J/cm²
@Temperature -30.0 °C23.8ft-lb/in²
@Temperature -22.0 °FEdgew 80*10*4 sp=62mm; ISO 179/1eUCharpy Impact, Notched0.600J/cm²
@Temperature -30.0 °C2.86ft-lb/in²
@Temperature -22.0 °FV-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA0.700J/cm²
@Temperature 23.0 °C3.33ft-lb/in²
@Temperature 73.4 °FV-notch Edgew 80*10*4 sp=62mm; ISO 179/1eAImpact Test5.00J
@Temperature 23.0 °C3.69ft-lb
@Temperature 73.4 °FInstrumented Impact Total Energy; ASTM D 3763Taber Abrasion, mg/1000 Cycles22.0
@Load 1.00 kg22.0
@Load 2.20 lbCS-17; SABIC MethodIzod Impact, Notched0.570J/cm
@Temperature -30.0 °C1.07ft-lb/in
@Temperature -22.0 °FASTM D 2560.600J/cm
@Temperature 23.0 °C1.12ft-lb/in
@Temperature 73.4 °FASTM D 256Izod Impact, Notched (ISO)6.00kJ/m²
@Temperature -30.0 °C2.86ft-lb/in²
@Temperature -22.0 °F80*10*4; ISO 180/1A7.00kJ/m²
@Temperature 23.0 °C3.33ft-lb/in²
@Temperature 73.4 °F80*10*4; ISO 180/1AElectrical PropertiesMetricEnglishCommentsVolume Resistivity>=1.00e+15ohm-cm>=1.00e+15ohm-cmASTM D 257>=1.00e+15ohm-cm>=1.00e+15ohm-cmIEC 60093Surface Resistance>=1.00e+15ohm>=1.00e+15ohmROA; IEC 60093Dielectric Constant3.30
@Frequency 1.00e+6 Hz3.30
@Frequency 1.00e+6 HzIEC 602503.30
@Frequency 50.0 - 60.0 Hz3.30
@Frequency 50.0 - 60.0 HzIEC 602503.70
@Frequency 1.00e+6 Hz3.70
@Frequency 1.00e+6 HzASTM D 1503.80
@Frequency 100 Hz3.80
@Frequency 100 HzIEC 602503.80
@Frequency 100 Hz3.80
@Frequency 100 HzASTM D 150Dielectric Strength16.0kV/mm
@Thickness 3.20 mm406kV/in
@Thickness 0.126 inin oil; IEC 60243-119.0kV/mm
@Thickness 3.20 mm483kV/in
@Thickness 0.126 inin air; ASTM D 14922.0kV/mm
@Thickness 1.60 mm559kV/in
@Thickness 0.0630 inin oil; IEC 60243-123.0kV/mm
@Thickness 0.800 mm584kV/in
@Thickness 0.0315 inin oil; IEC 60243-124.0kV/mm
@Thickness 1.60 mm610kV/in
@Thickness 0.0630 inin oil; ASTM D 149Dissipation Factor0.00100
@Frequency 50.0 - 60.0 Hz0.00100
@Frequency 50.0 - 60.0 HzIEC 602500.00200
@Frequency 100 Hz0.00200
@Frequency 100 HzIEC 602500.00200
@Frequency 100 Hz0.00200
@Frequency 100 HzASTM D 1500.0100
@Frequency 1.00e+6 Hz0.0100
@Frequency 1.00e+6 HzIEC 602500.0200
@Frequency 1.00e+6 Hz0.0200
@Frequency 1.00e+6 HzASTM D 150Arc Resistance60.0-120sec60.0-120secTungsten, PLC code 6; ASTM D 495Comparative Tracking Index>=125V>=125VIEC 60112175V175VIEC 60112175-250V175-250VPLC code 3; UL 746AHot Wire Ignition, HWI30.0-60.0sec30.0-60.0secPLC code 2; UL 746AHigh Amp Arc Ignition, HAI>=120arcs>=120arcssurface, PLC code 0; UL 746AHigh Voltage Arc-Tracking Rate, HVTR>=150mm/min>=5.91in/minPLC code 4; UL 746AThermal PropertiesMetricEnglishCommentsCTE, linear, Parallel to Flow25.0µm/m-°C
@Temperature -40.0 - 40.0 °C13.9µin/in-°F
@Temperature -40.0 - 104 °FASTM E 83125.0µm/m-°C
@Temperature -40.0 - 40.0 °C13.9µin/in-°F
@Temperature -40.0 - 104 °FISO 11359-225.0µm/m-°C
@Temperature 23.0 - 80.0 °C13.9µin/in-°F
@Temperature 73.4 - 176 °FISO 11359-2CTE, linear, Transverse to Flow89.0µm/m-°C
@Temperature -40.0 - 40.0 °C49.4µin/in-°F
@Temperature -40.0 - 104 °FASTM E 83189.0µm/m-°C
@Temperature -40.0 - 40.0 °C49.4µin/in-°F
@Temperature -40.0 - 104 °FISO 11359-2120µm/m-°C
@Temperature 23.0 - 80.0 °C66.7µin/in-°F
@Temperature 73.4 - 176 °FISO 11359-2Thermal Conductivity0.250W/m-K1.74BTU-in/hr-ft²-°FISO 8302Deflection Temperature at 0.46 MPa (66 psi)220°C428°FEdgew 120*10*4 sp=100mm; ISO 75/Be212°C
@Thickness 3.20 mm414°F
@Thickness 0.126 inunannealed; ASTM D 648Deflection Temperature at 1.8 MPa (264 psi)195°C383°FEdgew 120*10*4 sp=100mm; ISO 75/Ae200°C392°FFlatw 80*10*4 sp=64mm; ISO 75/Af200°C
@Thickness 3.20 mm392°F
@Thickness 0.126 inunannealed; ASTM D 648Vicat Softening Point200°C392°FRate B/50; ISO 306200°C392°FRate B/120; ISO 306200°C392°FRate B/50; ASTM D 1525220°C428°FRate A/50; ISO 306UL RTI, Electrical130°C266°FUL 746BUL RTI, Mechanical with Impact130°C266°FUL 746BUL RTI, Mechanical without Impact140°C284°FUL 746BFlammability, UL94V-2
@Thickness 0.400 mmV-2
@Thickness 0.0157 inUL 94V-0
@Thickness 0.710 mmV-0
@Thickness 0.0280 inUL 945VA
@Thickness 2.00 mm5VA
@Thickness 0.0787 inUL 94Oxygen Index32.0 %32.0 %LOI; ISO 4589Glow Wire Test960°C
@Thickness 1.00 mm1760°F
@Thickness 0.0394 inGlow Wire Flammability Index; IEC 60695-2-12Descriptive PropertiesBall Pressure Test, 125°C +/- 2°CPASSESIEC 60695-10-2Specific Volume, cm^3/g0.61ASTM D 792UV-light, water exposure/immersionF2UL 746C Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistent format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb'sterms of useregarding this information.Click hereto view all the property values for this datasheet as they were originally entered into MatWeb.